Polymaker PolyMide CoPa 1.75mm – Black (750g)

R1,246.00

Product Highlights

  • Easy to print.
  • High heat resistance.
  • Robust material.
  • High tensile strength.
  • Exceptional quality.
  • Balanced mechanical properties.
  • Nozzle Temperature 230˚C – 240˚C.
Availability: Out of stock

Description

Black – 1.75mm Polymaker PolyMide CoPa (750g)

Polymaker PolyMide CoPa  – Polymaker’s PolyMide™ CoPA 3D printing filament is based on a copolymer of Nylon 6 and Nylon 6,6. The filament combines excellent strength, toughness, and heat resistance of up to 180˚C. Manufactured with Polymaker’s Warp-Free technology, this 3D printing material brings engineering properties intrinsic to Nylon, along with supreme ease of printing.

Warp Free

PolyMide CoPA is engineered to give excellent dimensional stability during printing, with near-zero warping.

Easy Printing

Unlike other Nylon filaments, PolyMide CoPA is extremely easy to work with. It is compatible with most filament-based 3D printers with no heated chamber/bed required!

Strong & Touch

The outstanding mechanical strength and toughness make PolyMide CoPA the best choice of engineering material for your creative ideas!

Heat Resistant

With a high softening temperature of ~180 °C, PolyMide CoPA is one of the most heat resistant 3D printing materials in the market.

Technical Specifications
  • Net Weight: 1 Kg <± 20g (Typical <+ 20g)
  • Diameter (Tolerance): 2.85 mm ±0.05 mm
  • Nozzle Temperature: 250˚C – 270˚C
  • Printing Speed: 30mm/s – 50mm/s
  • Heated Bed: 25˚C – 70˚C
  • Recommended bed surface: Glass with glue
  • Cooling fan: Off
  • This material is hygroscopic, and it is recommended to dry at 80˚C for 12 hours before printing

Additional information

Weight 1.5 kg
Dimensions 24 × 21 × 8 cm
PRINT SETTINGS
Nozzle Temperature 250˚C – 270˚C
Printing Speed 30mm/s – 50mm/s
Bed Temperature 25˚C – 70˚C
Bed Surface Glass with glue
Cooling Fan OFF
MECHANICAL PROPERTIES
Young’s Modulus 2223 ± 199 Mpa
Tensile Strength 66.2 ± 0.9 Mpa
Bending Strength 97.0 ± 1.1 Mpa
Charpy Impact Strength 9.6 ± 1.4 kJ/m2
THERMAL PROPERTIES
Glass Transition Temperature 67˚C
Vicat Softening Temperature 180˚C
Melting Temperature 190˚C
It is highly recommended to use the PolyBox™ when printing with PolyMide™ CoPA and to store it in the resealable bag.
To ensure a good heat resistance of your printed part it is recommended to anneal your PolyMide™ CoPA 3d printed model.
Annealing settings: 70˚C for 2h